Influence of activation mode, fatigue, and ceramic interposition on resin cements' diametral tensile strength.

This study evaluated the influence of activation modes, on Diametral Tensile Strength (DTS) of dual cured resin cements subjected to a Mechanical Fatigue test (MF). Four dual-cured resin cements (RelyX UNICEM [U], RelyX ARC [A], ENFORCE [E] and Nexus 2 [N]) were activated by three different curing modes as follows: Self-Curing (SC), Dual Cure activation with photoactivation executed directly (DC) and Dual Cure activation with Photoactivation Through Porcelain (DCTP). After 24 hours, half of the sample was subjected to 30.000 fatigue cycles at 1 Hz frequency and 12 N load. Then, all specimens were subjected to DTS test in Instron Universal Testing Machine and data were analyzed by three-way ANOVA and Tukey's Test (5%). The results of DTS test means (MPa) and standard deviation, for each cement factor activated by SC, DC and DCTP was respectively: U (28.12 ± 5.29; 37.44 ± 6.49 and 40.10 ± 4.39), A (49.68 ± 8.42; 55.12 ± 5.16 and 63.43 ± 6.92), E (49.12 ± 3.89; 56.42 ± 8.88 and 56.96 ± 6.45) and N (61.89 ± 11.21; 59.26 ± 9.47 and 62.56 ± 10.93). Turkey's test indicated that DC is related to the highest DTS values; Nexus 2 DTS remained the same independently of activation mode and that the Porcelain disk interposition enhanced DTS only for RelyX ARC the ANOVA statistical test indicated that MF didn't alter the DTS values for all experimental groups. MF results clinical implication is that all cements tested exhibited, in an immediate loading, good cross linked bonds quality.

Aesthetic solution for ceramic restoration on cast metal core

Introduction: In order to satisfy the aesthetic desires of the population, by masking the restorations was the search for the evolution of restorative materials enabling the introduction of metal-free materials. But previous studies that have been made with metal structures often cannot be removed and therefore require devices that can be masked, because there is no desire for a total passage of light avoiding dim reflection of these funds. For these situations, you must opt for a ceramic system to provide a degree of opacity, without losing its characteristics of light transmission, reflectance and saturation. Case report: In case the patient had clinical a metal ceramic crown on the molten core element 21, it was confirmed radiographically the core could not be removed because it would fracture risk to the tooth. We chose to use an opaquer ceramic framework to prevent the passage of light over dark metal. The material of choice was zirconia ceramic by high flexural strength, allowing it to function as a framework for crowns. Conclusion: With the correct application of ceramic coverage on Caquetá noted that it is possible to mask the gray color of the metal through the knowledge of the optical material, the correct use of these properties, opacity and translucidus, and a close contact between dentists and prosthetic.

Introdução: A fim de satisfazer os anseios estéticos, da população, por mascarar as restaurações houve a busca pela evolução dos materiais restauradores possibilitando a introdução de materiais livres de metais. Porém trabalhos prévios que foram confeccionados com estruturas metálicas muitas vezes não podem ser removidos e, portanto, necessitam de artifícios para que possam ser mascarados, pois não há o desejo de uma total passagem de luz evitando a reflexão desses fundos escurecidos. Para estas situações, é necessário optar por um sistema cerâmico que apresente um grau de opacidade, sem perda de suas características de translucidez, refletância e saturação. Relato do caso: A paciente possuía uma coroa metalo-cerâmica sobre núcleo fundido no elemento 21, constatou-se radiograficamente que o núcleo não podia ser retirado, pois traria risco de fratura ao dente. Optou-se por utilizar uma cerâmica mais opaca de arcabouço para evitar a passagem de luz sobre o metal escurecido. O material de escolha foi à cerâmica de zircônia por apresentar alta resistência à flexão, permitindo que funcione como arcabouço para coroas unitárias. Conclusão: Com a correta aplicação de cerâmicas de cobertura sobre o casquete observou- se que é possível mascarar a cor acinzentada do metal através dos conhecimentos ópticos do material, a correta utilização dessas propriedades, opacidade e translucides, e um estreito contato entre dentista e protético.

How do the optical properties of the bulk fill posterior composites change after 2 years of simulated toothbrushing? / Como as propriedades ópticas de compósitos bulk fill se comportam após 2 anos de escovação simulada?

Objective: The objective of this study was to evaluate the alteration of the optical properties of bulk fill resin-based composites after two years of simulated toothbrushing. Material and Methods: Three high-viscosity bulk fill resin composites and one conventional sculptable resin composite (control) were analyzed. Five specimens of each resin composite were prepared, and roughness, color, translucency and gloss were evaluated initially and after one and two years of simulated toothbrushing. The specimens were submitted to electric simulated toothbrushing (14600 strokes / 100 g) using a commercially available soft bristle toothbrush and toothpaste slurry in a proportion of 1:2 by weight. The brushing scheme was of 40 cycles per day (2 cycles per second / 280 cycles in a week). The optical properties and the roughness data were analyzed by a multifactor analysis of variance (MANOVA) and a Tukey post hoc test. Results: The baseline and final values of Ra and Sa were submitted to linear regression analyses, all of which were performed at a significance level of 5%. Gloss and roughness presented statistical differences between the resin-time interactions in all composite resins. The gloss (72.5%) and roughness (89.4%) worsened significantly after brushing, but the authors didn't find statistically significant differences when evaluating translucency and color. Conclusion: Based in the results, it could be concluded that the simulated brushing degraded the gloss and roughness of the used high-viscosity bulk fill composites. (AU)

Objetivo: O objetivo deste estudo foi avaliar a alteração das propriedades ópticas de resinas compostas do tipo bulk fill após dois anos de escovação simulada. Material e Métodos: Foram analisadas três resinas compostas do tipo bulk fill de alta viscosidade e uma resina composta convencional (controle). Cinco corpos-deprova de cada resina composta foram preparados e a rugosidade, cor, translucidez e brilho foram avaliados inicialmente e após um e dois anos de escovação simulada. Os espécimes foram submetidos a escovação dental simulada (14.600 golpes / 100 g) utilizando-se escova de dentes de cerdas macias comercialmente disponíveis e uma pasta composta de dentifrício e água na proporção de 1:2 em peso. O esquema de escovação foi de 40 ciclos por dia (2 ciclos por segundo / 280 ciclos por semana). As propriedades ópticas e os dados de rugosidade foram analisados por uma análise de variância multifatorial (MANOVA) e um teste post hoc de Tukey. Resultados: Os valores iniciais e finais de Ra e Sa foram submetidos a análises de regressão linear, todas realizadas ao nível de significância de 5%. O brilho e a rugosidade apresentaram diferenças estatísticas entre as interações resina-tempo em todas as resinas compostas. O brilho (72,5%) e a rugosidade (89,4%) pioraram significativamente após a escovação, mas os autores não encontraram diferenças estatisticamente significativas ao avaliar a translucidez e a cor. Conclusão: Com base nos resultados, pôde-se concluir que a escovação simulada degradou o brilho e a rugosidade das resinas compostas do tipo bulk fill avaliadas. (AU)

Influence of activation mode, fatigue, and ceramic interposition on resin cements' diametral tensile strength

Abstract This study evaluated the influence of activation modes, on Diametral Tensile Strength (DTS) of dual cured resin cements subjected to a Mechanical Fatigue test (MF). Four dual-cured resin cements (RelyX UNICEM [U], RelyX ARC [A], ENFORCE [E] and Nexus 2 [N]) were activated by three different curing modes as follows: Self-Curing (SC), Dual Cure activation with photoactivation executed directly (DC) and Dual Cure activation with Photoactivation Through Porcelain (DCTP). After 24 hours, half of the sample was subjected to 30.000 fatigue cycles at 1 Hz frequency and 12 N load. Then, all specimens were subjected to DTS test in Instron Universal Testing Machine and data were analyzed by three-way ANOVA and Tukey's Test (5%). The results of DTS test means (MPa) and standard deviation, for each cement factor activated by SC, DC and DCTP was respectively: U (28.12 ± 5.29; 37.44 ± 6.49 and 40.10 ± 4.39), A (49.68 ± 8.42; 55.12 ± 5.16 and 63.43 ± 6.92), E (49.12 ± 3.89; 56.42 ± 8.88 and 56.96 ± 6.45) and N (61.89 ± 11.21; 59.26 ± 9.47 and 62.56 ± 10.93). Turkey's test indicated that DC is related to the highest DTS values; Nexus 2 DTS remained the same independently of activation mode and that the Porcelain disk interposition enhanced DTS only for RelyX ARC the ANOVA statistical test indicated that MF didn't alter the DTS values for all experimental groups. MF results clinical implication is that all cements tested exhibited, in an immediate loading, good cross linked bonds quality.

Influence of custom adaptation on the characteristics of fiber posts.

In this in vitro study, 3 experiments were conducted to evaluate the influence of customizing the apical portion on the characteristics of fiber posts. In the first experiment, 4 fiber posts were submitted to different custom adaptations (no customization, industrial shaping tool, diamond bur, or paper disc) and were observed with a scanning electron microscope to evaluate the micromorphologic changes. In the second experiment, 60 posts of different sizes were divided into 6 groups (n = 10): 0 (No. 0.5), 1 (No. 1), 2 (No. 2), 3 (No. 3), 4 (No. 4), and 5 (paper disc-remodeled No. 4). The posts were submitted to a 3-point bending test. In the third experiment, the crowns of 20 extracted, healthy permanent human canines were removed, and the teeth were endodontically treated, embedded in acrylic resin, and divided into 2 groups (n = 10): I (control), No. 4 posts cemented into post spaces prepared with a No. 4 drill; and II (test), remodeled No. 4 posts cemented into root spaces prepared with No. 2 and 4 drills. The posts were cemented with self-adhesive dual resin cement, and the specimens received direct resin crowns. Fracture strength was measured with a universal testing machine at 45 degrees until fracture. Results were submitted to analysis of variance (P ≤ 0.05). Customization of fiber posts with diamond burs or paper discs produced acceptable micromorphologic changes. Custom adaptation of fiber posts reduced their flexural strength, which remained at acceptable values. Teeth restored with customized fiber posts had greater fracture strength than those restored with intact posts. The results of this study indicated that post remodeling is a safe means to facilitate adaptation to root walls and preserve tooth structure.

Immediate Desensitization in Teeth Affected by Amelogenesis Imperfecta

Abstract The aim of this paper was to describe a clinical case of immediate dental desensitization using a self-etch adhesive system in an adolescent patient diagnosed with amelogenesis imperfecta (AI). AI was associated with severe tooth sensitivity, treated by the application of a universal adhesive system for desensitization of the teeth affected by AI. Reduction of tooth sensitivity was assessed using a visual analog scale during all reevaluations. The technique was effective for reducing tooth sensitivity. It was concluded that the adhesive system for tooth desensitization had an immediate effect and maintained its effectiveness during a 12-month follow-up period.

Resumo O objetivo deste estudo foi descrever uma técnica de dessensibilização dental imediata, usando o adesivo universal em paciente adolescente diagnosticado com amelogênese imperfeita. O paciente afetado pela amelogênese imperfeita apresentava dentes extremamente sensíveis, e foi submetido a aplicações de adesivo universal para dessensibilizar os dentes afetados por amelogênese imperfeita. A redução da sensibilidade dentária foi avaliada pela escala analógica visual durante todas as reavaliações. A técnica foi efetiva na redução da sensibilidade dental. Concluiu-se que o uso do sistema adesivo foi eficaz na imediata dessensibilidazação dentária e mantida após doze meses de avaliação.

Immediate Desensitization in Teeth Affected by Amelogenesis Imperfecta.

The aim of this paper was to describe a clinical case of immediate dental desensitization using a self-etch adhesive system in an adolescent patient diagnosed with amelogenesis imperfecta (AI). AI was associated with severe tooth sensitivity, treated by the application of a universal adhesive system for desensitization of the teeth affected by AI. Reduction of tooth sensitivity was assessed using a visual analog scale during all reevaluations. The technique was effective for reducing tooth sensitivity. It was concluded that the adhesive system for tooth desensitization had an immediate effect and maintained its effectiveness during a 12-month follow-up period.

Influence of surface treatment on shear bond strength of orthodontic brackets

INTRODUCTION: The shear bond strength of orthodontic brackets bonded to micro-hybrid and micro-particulate resins under different surface treatment methods was assessed. METHODS: Two hundred and eighty test samples were divided into 28 groups (n = 10), where 140 specimens were filled with Durafill micro-particulate resin and 140 with Charisma composite. In 140 samples, a coupling agent (silane) was applied. The surface treatment methods were: Phosphoric and hydrofluoric acid etching, sodium bicarbonate and aluminum oxide blasting, stone and burs. A Universal Instron Machine was used to apply an occlusal shear force directly to the resin composite bracket surface at a speed of 0.5 mm/min. The means were compared using analysis of variance and multivariate regression to assess the interaction between composites and surface treatment methods. RESULTS: Means and standard deviations for the groups were: Sodium bicarbonate jet 11.27±2.78; burs 9.26±3.01; stone 7.95±3.67; aluminum oxide blasting 7.04±3.21; phosphoric acid 5.82±1.90; hydrofluoric acid 4.54±2.87, and without treatment 2.75±1.49. An increase of 1.94 MPa in shear bond strength was seen in Charisma groups. Silane agent application reduced the Charisma shear bond strength by 0.68 Mpa, but increased Durafill means for bicarbonate blasting (0.83), burs (0.98) and stone drilling (0.46). CONCLUSION: The sodium bicarbonate blasting, burs and stone drilling methods produced adequate shear bond strength and may be suitable for clinical use. The Charisma micro hybrid resin composite showed higher shear bond means than Durafill micro particle composite.

INTRODUÇÃO: foram avaliadas as forças de cisalhamento após colagem de braquetes ortodônticos em superfícies resinosas microparticuladas ou micro-híbridas, após diferentes tratamentos de superfície. MÉTODOS: foram utilizados 280 corpos de prova, divididos em grupos de 10 elementos cada, sendo 140 preenchidos com resina microparticulada Durafill e 140 com resina micro-híbrida Charisma. Os tratamentos de superfície envolveram: ácido fosfórico, ácido fluorídrico, jato de bicarbonato de sódio, jato de óxido de alumínio, pedra e broca. A silanagem foi utilizada em metade dos grupos. O cisalhamento foi realizado com a máquina universal de testes EMIC DL 10000 MF, com célula de 10kg e velocidade de 0,5mm/min. As comparações entre as forças de cisalhamento foram obtidas por meio da análise de variância, e o grau de interação entre os tipos de compósito e o preparo de superfície foram obtidos por meio de uma regressão multivariada. RESULTADOS: as médias e desvios-padrão foram: jato de bicarbonato = 11,27 ± 2,78; broca = 9,26 ± 3,01; pedra = 7,95 ± 3,67; jato de óxido de alumínio = 7,04 ± 3,21; ácido fosfórico = 5,82 ± 1,90; ácido fluorídrico = 4,54 ± 2,87; e sem preparo = 2,75 ± 1,49. Um acréscimo de 1,94MPa foi obtido com o uso do compósito Charisma. A silanagem reduziu em 0,68MPa as médias do compósito Charisma, e aumentou o Durafill com uso do jato de bicarbonato (0,83), broca (0,98) e pedra (0,46). CONCLUSÃO: os preparos com jato de bicarbonato, broca e pedra obtiveram médias de forças apropriadas para colagem. O compósito Charisma apresentou forças de maior intensidade que as da resina Durafill.

Influência da espessura do filme de cimento na resistência de união de pinos reforçados por fibras cimentadas em canais radiculares / Influence of the cement film thikness on the bond strenght of fiber reinforced posts cemented in root canals

Atualmente, a cimentação adesiva de pinos pré-fabricados reforçados por fibras em condutos radiculares é um procedimento comum na prática clínica. No entanto, muitas vezes o pino não se adapta ao conduto e um desgaste excessivo de estrutura dentária é realizado no intuito de promover uma melhor adaptação, ou um pino de menor diâmetro é selecionado, formando um filme de cimento muito espesso. Sendo assim, o presente estudo visa colaborar com os profissionais da área de Odontologia por meio de uma revisão de literatura que possui como objetivo discutir sobre a união de pinos cimentados em canais radiculares, além de abordar sobre pinos reforçados por fibras e cimentação adesiva

Currently, adhesive cementation of prefabricated fber reinforced posts in root canals is a common procedure in clinical practice. However, often the post does not ft precisely to the root canal and excessive wear of tooth structure is carried out in order to promote a better ft, or a post with smaller diameter is selected creating greater cement flm thickness. Therefore, this study aims to collaborate with professionals in dentistry through a literature review that discuss the influence of cement flm thickness on the bond strength of posts cemented in root canals, besides addressing on fber reinforced posts and adhesive cementation.

Cimentação adesiva de pinos fibrorreforçados / Adhesive cementation of fiber reinforced posts

Os pinos resinosos fibrorreforçados cimentados adesivamente desempenham importante papel no tratamento restaurador contemporâneo, sendo considerados substitutos dos pinos metálicos pré-fabricados ou fundidos. O objetivo deste trabalho é revisar a literatura acerca da cimentação adesiva desses pinos, apresentando os tipos de cimento disponíveis e sua estratégia adesiva envolvida, assim como as dificuldades inerentes à cimentação no interior de condutos radiculares.

The adhesively bonded fiber reinforced composite posts (FRCP) play an important role in the contemporary restorative dentistry treatment, being considered as substitutes for prefabricated or cast metal posts. The aim of this article is to review the existing literature regarding FRCP, the available cement options and their adhesive strategy, along with the inherent difficulties to root canal cementation.

Mechanical and microstructural properties of a nickel-chromium alloy after casting process

Introduction: There is a growing concern on the development of adequate materials to interact with the human body. Several researches have been conducted on the development of biomaterials for dental applications. Objective: This study aimed to determine the microstructural and mechanical properties of a nickel- based alloy, after the casting process. Material and methods: The alloy was melted through lost wax technique and centrifugation, by using blowtorch with liquefied petroleum gas. To evaluate the mechanical properties, tensile bond strength and microhardness tests were performed. The microstructural characterization was performed using scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). Statistical analyses were performed on microhardness results, through Student t test. A program for digital image processing was used to determine the percentage of the existing phases. Results and Conclusion: The tensile strength was higher than that reported by the manufacturer, 559.39±25.63MPa versus 306 MPa, respectively. However, the yield strength was slightly lower, 218.71±29.75 MPa versus 258 MPa, reported by the manufacturer. The microhardness tests showed about 70 HV, far above the value informed by the manufacturer (21 HV). It can be affirmed with 95% confidence interval that the casting process did not alter the material's hardness. The alloy's microstructure is formed by a matrix with dendritic aspect and gray color and a second white interdendritic phase with equally distributed precipitates as well as porosities. EDS tests showed that the matrix is rich in nickel and chromium, the interdendritic second phase is rich in molybdenum and the precipitates in titanium or silicon. The matrix represents 86% of the area and the second phase 12%.

Tratamento estético restaurador com o uso de resina composta em dentes anteriores associado a clareamento dentário prévio: relato de caso / Esthetic restorative treatment using resin composite in anterior teeth associated toprevious dental bleaching: clinical case report

O tratamento estético utilizando o clareamento dentário e restaurações com resina composta é uma excelente alternativa para a obtenção de um belo sorriso. A procura da estética pelos pacientes tem sido cada vez mais frequente, em busca de dentes claros e de um sorriso harmonioso. O clareamento dentário proporciona uma estética mais favorável, porém já é bastante elucidado que os agentes clareadores atuam somente na estrutura dentária, e não nos materiais restauradores, no que diz respeito à descoloração. Por isso, muitas vezes há a necessidade de substituir restaurações de resina composta após o tratamento clareador. O presente artigo apresenta o relato de um caso clínico em que foi realizado o clareamento dentário em consultório com peróxido de hidrogênio a 20 por cento com posterior substituição das restaurações de resina composta pela técnica estratificada, utilizando um compósito mecrohíbrido. O resultado clínico foi adequado e satisfatório, oferecendo um belo sorriso ao paciente, o que demonstra a possibilidade de se realizar os dois procedimentos, visando melhorar a estética, através de um sorriso harmonioso.

The esthetic treatment using dental bleaching and resin composite restorations is an excellent alternative to obtain a beautiful smile. Patients' demands for cosmetic have been much more often in search of bleached teeth and a bright harmonic smile. Dental bleaching provides a beautiful smile, but it is quite known that bleaching agents act only in the tooth structure and do not in restorative materials. Therefore, there is often the need to replace resin composite restorations after bleaching. This article presents a case report in which was performed a dental office bleaching with hydrogen peroxide at 20%, with subsequent replacement of resin composite restorations through the stratified technique using a micro-hybrid resin composite. Clinical outcome was adequate and satisfactory offering a beautiful smile to the patient. This demonstrates the possibility of performing both procedures, and therefore improve esthetics as the proportion of a harmonious smile.

Influência do processo de fabricação de reconstruções metalocerâmicas na microestrutura de liga níquel-cromo / Manufacture process of metal-ceramic reconstructions influence on the nickel-chromium alloy microestructure

Introdução: Durante a fabricação de reconstruções dentárias, que utilizam sistemas metalocerâmicos, é utilizado um tratamento térmico para promover a adesão da porcelana ao metal. Entretanto, sabe-se que tratamentos térmicos podem alterar a microestrutura do material metálico, modificando suas propriedades. Objetivo: Este trabalho objetivou avaliar as possíveis modificações causadas na microestrutura de liga à base de níquel-cromo utilizada para reconstruções metalocerâmicas, quando a mesma é submetida ao tratamento térmico para adesão da porcelana.Material e método: O material pesquisado foi dividido nos grupos CR, F e TT, que representam, respectivamente, o material como recebido do fabricante, o material apenas submetido ao processo de fundição e o material após fundição e tratamento térmico. Os grupos CR e F foram submetidos à análise química quantitativa. A caracterizaçãomicroestrutural dos três grupos foi realizada através da técnica de microscopia eletrônica de varredura, com um sistema de Energy Dispersive Spectroscopy. Técnicas de análise e processamento digital de imagens foram aplicadas às micrografias dos grupos F e TT, para determinação de possíveis modificações quantitativas nas fases presentes. Resultado: A microestrutura da liga era formada por uma matriz de estrutura dendrítica de coloração cinza, rica em níquel; uma segunda fase interdendrítica de coloração branca e aspecto rendilhado, rica em molibidênio, e precipitados de coloração preta, podendo ser ricos em silício ou titânio. Também foram identificadas porosidades.Conclusão: A microestrutura após o processo de fundição apresentou um tamanho da fase interdendrítica menor. Não foram identificadas mudanças na microestrutura e na composição química das fases após o tratamento térmico.

Introduction: Manufacturing process of metal-ceramic dental reconstructions systems includes heat treatment to promote adhesion of the porcelain in the metal. However, it is known that heat treatment can promote changes in the microstructure of metallic materials, thereby affecting their properties. Objective: This work evaluated themicrostructure stability of dental quality nickel base alloy submitted to the heat treatment aiming at achieving porcelain adhesion. Material and method: The samples divided into three sets, CR, F and TT, representing,respectively, the material received from the manufacturer, the material just before the casting process and the material after casting end heat treatment. The CR and F sample sets were submitted to quantitative chemical analysis. The samples of CR, F and TT sets was submitted to the microstructural characterization by scanning electron microscopy and energy dispersive spectroscopy. Digital images processing techniques were applied to micrographics of F and TT sets to determine the changes in the material microstructure before and after heat treatment. Result: The alloy microstructure exhibits a gray dendritic structure in a clear matrix, rich in nickel, and a white inter-dendritic second phase, rich in molybdenum, with scattered precipitates, rich in titanium or silicon,and porosity. Conclusion: The microstructure has an average size of the interdendritic phase less than the alloy after casting. Changes in the microestructure and in the chemical composition of each phase were not identified, whether before nor after thermal treatment.

Emprego racional de compósitos com matriz de silorano / Rational use of silorane-based composites

As restaurações diretas de compósitos em dentes posteriores são cada vez mais usadas, devido ao maior interesse pela estética, à abordagem restauradora conservadora e à melhora das propriedades dos materiais. A tensão de contração de polimerização desses materiais pode gerar má integridade marginal, sensibilidade pós-operatória, microinfiltração e manchamento marginal. Visando à redução desses problemas, foi desenvolvido um compósito com um sistema monomérico não baseado em dimetacrilatos: o silorano. O novo compósito tem mostrado boas propriedades mecânicas, estabilidade no meio oral e baixa contração de polimerização. Por ser um novo produto, há carência de estudos clínicos controlados de longo prazo a tal respeito. Assim, o objetivo deste estudo é revisar a literatura e descrever um caso clínico em que se utiliza esse novo material, o Filtek P90 (3M ESPE)

Direct composite restorations in posterior teeth are increasingly used due to the increasing interest on esthetics, conservative approach and the improved properties of latest restorative material. Polymerization shrinkage stresses of such materials are reported to be associated to poor marginal integrity, postoperative sensitivity, microleakage and marginal discoloration. In an attempt to minimize these problems, a new monomer system was developed, which is not based on dimethacrylates: Siloraneo. It has been shown that this novel composite has good mechanical properties, stability in oral environment and low polymerization shrinkage. Because it has been recently introduced, there is a lack of long-term controlled clinical studies about the latter property. The aim of this study was to review the literature and to report a clinical case using a novel material (Filtek P90, 3M ESPE)

Uso de sistema de fibras de reforço em prótese adesiva posterior: relato de caso clínico / Reinforcerd fibers system use in posterior adhesive prothesis: clinical case report

A utilização de resinas associadas a fibras de reforço é uma excelente alternativa para casos de prótese adesiva. Este trabalho apresenta um caso clínico em que foi confeccionada uma prótese fixa reforçada do sistema de pônticos e fibras de vidro Fibrex-Lab (Angelus, Brasil) associada à resina composta Natural Look (DFL, Brasil). O resultado clínico foi altamente satisfatório, oferecendo função e estética ao paciente, o que demonstra a possibilidade da utilização das fibras de vidro como alternativa às ligas metálicas e cerâmicas reforçadas para subestruturas em situações clínicas bem indicadas de próteses parciais fixas. Dessa forma, o trabalho executado foi muito útil para que o emprego desses materiais permita aos dentistas clínicos a escolha de novas alternativas seguras para reabilitar sorrisos.

Restauração de dentes tratados endodonticamente com pino de fibra de vidro e acessório em canais amplos / Fiber glass post and accessory post to restore endodontically treated teeth with large root canal

Os pinos de fibra de vidro têm sido extensivamente utilizados em dentes com grande perda de estrutura dentária e canais endodonticamente tratados. Por apresentar seção circular, mesmo com diâmetros diversos, sua linha de cimentação torna-se muito espessa em canais mais elípticos ou alargados. Tal condição poderia aumentar o potencial para a microinfiltração, além de diminuir a resistência à fratura do núcleo. Este artigo mostra a resolução do caso clínico de um incisivo lateral superior com conduto radicular amplo tratado endodonticamente, a partir do emprego de um retentor intra-radicular de fibra de vidro cônico associado a um pino acessório, com objetivo de diminuir a linha de cimentação e aumentar a longevidade do procedimento restaurador.

Influência da remoção do colágeno associado a um adesivo autocondicionante na infiltração marginal de restaurações classe V / Influence of collagen removal in association with a one-step adhesive system on microleakage of class V

O objetivo deste trabalho foi avaliar a infiltração marginal em restaurações classe V de resina composta utilizando ácido fosfórico a 35 por cento e hipoclorito de sódio a 10 por cento, previamente ao adesivo autocondicionante (Prompt L-Pop - Espe). Sessenta preparos foram realizados em vinte molares humanos. Cada dente recebeu três preparos distribuídos em um dos três grupos: 1) sistema adesivo Propmt L-Pop seguindo recomendações do fabricante; 2) condicionamento com ácido fosfórico por 30 segundos e adesivo Prompt L-Pop; 3) condicionamento com ácido fosfórico seguido de aplicação de hipoclorito de sódio e adesivo Prompt L-Pop. Os resultados não evidenciaram diferença estatística entre os grupos

Comparative SEM evaluation of penetration of adhesive systems in human dentin with a non-rinse conditioner and a self-etching primer

O objetivo desse estudo foi comparar o efeito de um adesivo autocondicionante e de um ácido não lavável quanto a profundidade de penetração na dentina de dentes humanos, através da observação em Microscopia Eletrônica de Varredura (MEV). Quinze terceiros molares tiveram a dentina exposta, cortando-se a face oclusal, planificados com lixa d'água 600, cortados transversalmente e distribuídos em 6 grupos de 5 cada: grupo 1 - Prime Bond NT (NT), controle negativo; grupo 2 - ácido fosfórico 37% + Prime Bond NT (PANT), controle positivo; grupo 3 - Non-Rinse Conditioner (NRC) + Prime Bond NT (NRCNT); grupo 4 - NRC + Prime Bond 2.1 (NRCPB); grupo 5 - NRC + Scotch Bond MP (NRCSB) e grupo 6 - Prompt L-Pop (PLP). Todos foram recobertos com Dyract AP. Os fragmentos dentários foram descalcificados com HCl a 10% e NaOH a 5% e as réplicas em resina examinadas em MEV. Três examinadores calibrados avaliaram as fotomicrografias e atribuíram escores de 0 = sem penetração a 3 = penetração máxima. Os testes de Kruskal-Wallis e Mann-Whitney (P<0,05) evidenciaram três grupos homogêneos {NT, NRCPB, NRCSB e PLP}; {NRCNT} e {PANT}. Os autores concluíram que o sistema adesivo autocondicionante e o ácido não lavável apresentaram menor penetração em dentina do que o sistema adesivo convencional.

Efeito do jato profilático de bicarbonato de sódio sobre a superfície de materiais restauradores estéticos / The effect of the prophylactic jet on the surface of restorative materials

Foi avaliado, em Microscopia Eletrônica de Varredura, o efeito do jato profilático de bicarbonato de sódio sobre os materiais: Durafil, Z100, TPH, Concise, Heliomolar Chelon-fil e Dyract AP, com e sem a proteção do selante de superfície Fortify, por 15, 30 ou 60 segundos. Os autores concluíram que a aplicação do jato altera a superfície dos materiais. A partir de 30 segundos, todos os materiais tiveram o contorno alterado com perda de substância